潜江电子材料汉高ABLESTIKJM7000导电胶,汉高导电胶

ABLESTIK JM7000具有高可靠性，低空洞特点，耐高温可达370度。

常用超大规模集成电路封装，陶瓷焊接封装和焊接密封封装

乐泰EA 3335透明UV耐热耐水耐腐蚀光通讯光路胶

粘度 5000-7000cp 固化条件 UV 硬度80shoreA Tg值 135℃ CTE,低于Tg温度59ppm/℃ CTE,Tg值温度 ppm/℃

透明，UV快速固化，良好的耐热，耐水，耐化学腐蚀性，低挥发。

乐泰ABLESTIK JM 7000
氰酸酯
外观银
治疗热治疗
填料型银
●良好的附着力
●水分低
●离子杂质低
●可靠性高
●空洞少
●导电
●导热
应用模连接
基板氧化铝，镀金氧化铝

LOCTITE ABLESTIK JM 7000 die attach adhesive has been
formulated for use in high throughput die attach applications. This
material has been used successfully on rigid substrates with die sizes
up to 700 mils.
LOCTITE ABLESTIK JM 7000 has been approved by DESC and
Rome Laboratory for military products.
TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5
BLETHERM 2600AT高导热导电银胶 黏 度： 8.5 PaS 剪切强度： - Mpa 工作时间： 1440 min 工作温度： - ℃ 保 质 期： 12 个月 固化条件： 30分钟升到200°C + 15分钟 @ 200°C 主要应用： 大功率LED

HENKEL ABLETHERM 2600AT粘合剂是一款特别为芯片需要高散而开发的芯片粘接胶,如大功率和和散热元气件. 本粘合剂是一种特的悬浮液-银和树脂颗粒悬浮在溶剂载体中. 一旦胶水完全固化,溶剂也会干掉, 本粘合剂含有很高比重的银. 本品主要用于高功率,高导热的大功率发光二极管.